Table 3 Composition, Initial gloss, calculated relative gloss decay and state of chalking for experiment II
From: Investigating the effect of artists’ paint formulation on degradation rates of TiO2-based oil paints
Composition | Responses | ||||||
|---|---|---|---|---|---|---|---|
A: ΦUA | B: ΦCR(inorg) | C: ΦZnO | D: ΦOil | E: ΦAlSt | Initial gloss | Δgloss 750 rel | State of chalking at Iend |
0.00 | 0.10 | 0.09 | 0.81 | 0 | 57.03 | 25.59 | 0 |
0.14 | 0.03 | 0.03 | 0.80 | 0 | 44.27 | 36.90 | 1 |
0.07 | 0.07 | 0.00 | 0.84 | 0.02 | 77.87 | 7.46 | 0 |
0.10 | 0.09 | 0.00 | 0.81 | 0 | 78.37 | 9.49 | 0 |
0.19 | 0.00 | 0.00 | 0.79 | 0.02 | 7I7 | 60.33 | 1 |
0.00 | 0.00 | 0.20 | 0.80 | 0 | 42.60 | 52.76 | 1 |
0.00 | 0.20 | 0.00 | 0.80 | 0 | 82.27 | 2.94 | 0 |
0.12 | 0.00 | 0.00 | 0.88 | 0 | 83.23 | 49.03 | 0.5 |
0.13 | 0.02 | 0.00 | 0.82 | 0.02 | 74.30 | 34.95 | 0.5 |
0.00 | 0.05 | 0.09 | 0.86 | 0 | 78.53 | 15.60 | 0.5 |
0.10 | 0.00 | 0.00 | 0.90 | 0 | 82.30 | 21.98 | 0.5 |
0.00 | 0.07 | 0.07 | 0.84 | 0.02 | 54.83 | 22.10 | 0 |
0.07 | 0.00 | 0.07 | 0.84 | 0.02 | 40.63 | 33.59 | 1 |
0.06 | 0.07 | 0.06 | 0.80 | 0 | 56.50 | 22.03 | 0 |
0.07 | 0.00 | 0.07 | 0.84 | 0.02 | 35.33 | 43.27 | 1 |
0.10 | 0.08 | 0.01 | 0.78 | 0.02 | 23.17 | 60.72 | 0 |
0.03 | 0.04 | 0.04 | 0.90 | 0 | 83.80 | 19.21 | 0 |
0.00 | 0.00 | 0.13 | 0.87 | 0 | 75.20 | 29.85 | 0.5 |
0.11 | 0.01 | 0.08 | 0.78 | 0.02 | 33.27 | 34.98 | 1 |
0.01 | 0.09 | 0.10 | 0.78 | 0.02 | 41.97 | 21.02 | 0 |
0.00 | 0.13 | 0.00 | 0.87 | 0 | 87.87 | 1.07 | 0 |
0.00 | 0.17 | 0.01 | 0.79 | 0.035 | 48.43 | 48.14 | 0 |
0.00 | 0.00 | 0.19 | 0.79 | 0.02 | 15.60 | 59.40 | 1 |
0.00 | 0.00 | 0.18 | 0.79 | 0.035 | 16.50 | 59.58 | 1 |
0.05 | 0.05 | 0.05 | 0.85 | 0 | 45.93 | 31.99 | 0 |
0.00 | 0.07 | 0.07 | 0.84 | 0.02 | 43.27 | 24.75 | 0 |
0.00 | 0.20 | 0.00 | 0.78 | 0.02 | 71.8 | 2.89 | 0 |
0.09 | 0.00 | 0.10 | 0.81 | 0 | 36.63 | 41.72 | 1 |
0.05 | 0.05 | 0.05 | 0.85 | 0 | 50.77 | 29.12 | 1 |
0.20 | 0.00 | 0.00 | 0.78 | 0.02 | 64.83 | 56.31 | 1 |