Multi-methodical study of Early Modern Age archaeological glazed ceramics from Prague

Kloužková, Alexandra; Kohoutková, Martina; Kolářová, Mária; Blažková, Gabriela; Šefců, Radka; Dvořáková, Pavla; Bajeux Kmoníčková, Martina

doi:10.1186/s40494-020-00423-x

Heritage Science

Table 4 Chemical composition of the glazes of all studied finds analysed before the chemical cleaning of corrosion layers (wt%)

From: Multi-methodical study of Early Modern Age archaeological glazed ceramics from Prague

Sample	SiO₂	Al₂O₃	Fe₂O₃	TiO₂	CaO	MgO	K₂O	Na₂O	P₂O₅	SO₃	Cl	MnO	CuO	ZnO	ZrO₂	BaO	PbO	SnO₂	Sb₂O₃	Bi₂O₃
1 G	22	6	5	0	4	0.3	0.4	0.5	7	1	0	0	0	2	0	0	52	0	0	0
2 G	42	6.9	1.1	0.5	3.5	0.3	2	0.6	3.9	1.8	0.7	0	2.2	0.01	0.03	0.1	34	0	0.2	0
3 G	30	2.4	1.1	0.3	1.4	0.3	0.4	0.2	0.3	4.2	2.8	0.04	2.5	0.04	0	1.5	52	0	0.1	0
4 G	8	3	1	0	52	0.8	0.2	1	28	3	0.3	0	0	0.2	0.1	0	4	0	0	0
5 G	24	3	6	0	3	0.3	1	1	8	1	1	0	0	1	0	0	51	0	0	0.2
6 G	36	1	6	0	18	0.3	0.4	1	19	1	3	0	0	4	0	0	40	0	0	0
7 G	38	4.8	0.9	0.3	2.7	0.8	1.7	1	3.5	2.3	1.1	0	3.5	0.02	0	0.1	39	0	0.2	0.1
8 G	23	3	5	0	0.3	0.3	0.3	0.2	0.4	0.5	0.1	0	0	1	0	0	66	0	0	0
9 G	16	9	10	0	14	0.4	0.2	0.3	16	1	1	0	0	0.3	0	0	46	0	0	0
10 G	26	5	1	0	2	0.8	1	0.4	2	0.3	0	0	2	0	0	0	61	0	0	0
11 G	23	4	5	0	13	0.6	1	1	10	1	0.5	0	0	0	0	0	43	0	0	0
12 G	13	4	4	2	14	0.7	1	1	1	9	0	0	1	1	0.1	6	39	4	0	0
13 G	33	5	1	1	2	0.5	1	0.4	6	2	0.3	0	2	0.1	0.2	0	48	0	0	0
14 G	16	7	3	1	9	0.5	0.6	0.5	0.1	3	0.4	0	0	2	0	0	58	0	0	0
15 G	35	8	4	1	1	0.8	0.4	0.3	0.3	0.1	0	0	0	0	0.2	0	49	0	0	0
16 G	33	12	2	2	2	0.5	1	0.4	0.4	2	1	0	0	1	0.2	1	41	0	0	0
17 G	27	8	3	1	1	0.5	1	0	0.1	0.3	0	0	0	0	0.2	0	58	0	0	0
18 G	12	2	1	0	34	0.5	0.3	0.5	16	1	0.3	0	0	0.3	0	0	32	0	0	0
19 G	12	4	1	1	21	0.4	0.3	0.3	17	1	0.3	0	0.2	1	0	0	40	0	0	0
20 G	28	6	1	0.3	1	0.6	1	0.4	0.2	1	0	0	0	0.1	0	0	62	0	0	0
21 G	36	2	0.4	0	2	0.3	0.4	0.5	0.2	2	2	0	5	0	0	0.5	50	0	0	0
22 G	10	3	1	0.3	28	0.3	0.5	1	19	2	1	0	0.1	0	0.1	0	34	0	0	0
23 G	27	6	2	0	1	0.3	0.3	0.5	0.2	0.3	0	0	0	1	0	0	61	0	0	0
24 G	21	8	2	1.5	3	0.5	0.6	0.3	1	0.8	0.1	0	0.6	0.1	0	0.2	61	0	0	0
25 G	29	5	2	1	1	0.3	0.3	0.3	0.1	0.4	0.3	0	0	0.1	0	0	61	0	0	0
26 G	25	8	2	1	1	0.4	0.5	0.4	0.3	0.4	0	0	0	0	0	0	61	0	0	0
27 G	24	8	4	1	4	0.5	2	1	0.3	3	0.5	0	0	0.3	0.2	0	51	0	0	0
28 G	25	6	1	1	0.7	0.4	0.5	0.3	0.2	2	0	0	2	0	0	0	62	0	0	0
29 G	18	10	1.3	0.5	1.9	0.8	0.7	0.6	0.3	0.9	0.5	0	0.5	0	0	0	64	0	0	0
30 G	6	1	8	0	0	0.2	0	0.9	0.3	21	3	0	0	0	0	0	57	4.4	0	0
31 G	22	6	4	0.5	1	0.4	0.5	0.5	1	0.8	0	0	0	0.4	0	0	63	0	0	0
32 G	34	12	3	1	3.5	1	0.5	0.3	2	0.6	0.1	0	0.1	0	0	0	42	0	0	0
33 G	14	2	1	0	5	0.3	1	0.3	1	3	1	0	3	0.1	0	0	70	0	0	0
34 G	13	3	2	0	2	0.4	1	1	1	13	1	0	3	0	0.2	0	59	2	0	0
35 G	7	1	4	0	2	0.4	0.3	1	2	17	1	0	2	0.3	0	0	48	15	0	0
36 G	11	4	3	0	43	1	0.2	0.5	0.6	2	0.3	1	0.2	1	0.1	0	33	0	0	0
37 G	14	6	2.5	0.7	41	1	0.3	0	2.1	3	0.1	0	0.2	0	0	0	29	0	0	0
38 G	25	8	1	0.8	4	1	0.9	0.5	2	0.6	0.1	0	0.5	0	0	0	55	0	0	0
39 G	24	6.7	1.2	0.8	7.3	0.5	0.7	0.7	3.2	0.5	0.4	0	0.3	0	0	0	54	0	0	0
40 G	23	9	1.3	0.7	5	0.6	0.4	0.6	4	0.6	0	0	0	0	0	0	55	0	0	0