Position No. | Ratio | Na2O | MgO | Al2O3 | SiO2 | K2O | CaO | TiO2 | Fe2O3 | MnO | P2O5 | Possible phase |
---|---|---|---|---|---|---|---|---|---|---|---|---|
P1 | wt% | Â | 15.45 | 3.84 | 51.42 | Â | 28.49 | Â | 0.79 | Â | Â | Diopside |
mol% | Â | 21.55 | 2.10 | 47.74 | Â | 28.34 | Â | 0.28 | Â | Â | ||
P2 | wt% | 1.09 | 0.86 | 26.12 | 55.31 | 2.21 | 13.49 | Â | 0.91 | Â | Â | Anorthite |
mol% | 1.18 | 1.45 | 17.24 | 61.97 | 1.58 | 16.19 | Â | 0.38 | Â | Â | ||
P3 | wt% | 0.42 | 0.76 | 7.83 | 33.93 | 3.56 | 30.31 | Â | 1.73 | 0.70 | 20.76 | Calcium phosphate |
mol% | 0.48 | 1.35 | 5.44 | 39.98 | 2.68 | 38.26 | Â | 0.77 | 0.70 | 10.35 | ||
P4 | wt% | 0.30 | 5.15 | 10.83 | 60.30 | 5.07 | 9.23 | 0.46 | 5.11 | 2.25 | 1.30 | Glass |
mol% | 0.31 | 8.36 | 6.89 | 65.15 | 3.49 | 10.68 | 0.37 | 2.07 | 2.06 | 0.59 |