PGAA | XRF | NAA | |
---|---|---|---|
H | 5430 ± 380 | ||
С | 137000 ± 25000 | ||
Mg | 26400 ± 4300 | 24000 ± 6200 | |
Al | 12700 ± 2000 | 15400 ± 900 | |
Si | 19000 ± 2000 | 24100 ± 1500 | |
S | 599 ± 272 | 758 ± 165 | |
Cl | 129 ± 11 | ||
K | 1870 ± 530 | 2460 ± 140 | 1450 ± 100 |
Ca | 310000 ± 20000 | 364000 ± 2000 | 282000 ± 37000 |
Sc | 1.31 ± 0.12 | ||
Ti | 454 ± 23 | 246 ± 57 | |
Mn | 341 ± 29 | ||
Fe | 7740 ± 1020 | 7500 ± 400 | 5840 ± 360 |
Co | 1.96 ± 0.23 | ||
Ni | 5.12 ± 0.38 | ||
Cu | 10.6 ± 2.4 | ||
Zn | 11.7 ± 3.3 | 10.8 ± 0.9 | |
As | 0.724 ± 0.040 | ||
Br | 1.31 ± 0.39 | ||
Rb | 4.17 ± 1.08 | ||
Zr | 19.8 ± 6.8 | ||
Mo | 0.259 ± 0.042 | ||
Sb | 0.101 ± 0.044 | ||
Cs | 0.0461 ± 0.0128 | ||
Ba | 94.8 ± 20.2 | ||
La | 8.49 ± 0.47 | ||
Ce | 17.1 ± 1.1 | ||
Nd | 3.54 ± 0.74 | ||
Sm | 1.76 ± 0.19 | 1.34 ± 0.15 | |
Eu | 0.297 ± 0.027 | ||
Gd | 1.28 ± 0.17 | ||
Tb | 0.160 ± 0.017 | ||
Yb | 0.313 ± 0.032 | ||
Lu | 0.062 ± 0.006 | ||
Hf | 0.615 ± 0.145 | ||
Ta | 0.121 ± 0.016 | ||
W | 0.145 ± 0.034 | ||
Au | 0.00331 ± 0.00079 | ||
Th | 1.09 ± 0.10 | ||
U | 0.467 ± 0.040 |