Table 3 Bending test results of the different specimens tested
Specimens | Printing material | Orientation | Filling density (%) | Printing time per specimen | Bending strain yield strength | Bending modulus [MPa] | Bending stress [MPa] |
|---|---|---|---|---|---|---|---|
PH10 | PLA Polylactic acid | Horizontal 0° | 10 | 54 min | 0.031 | 2216 | 80 |
PH50 | PLA Polylactic acid | Horizontal 0° | 50 | 58 min | 0.033 | 2405 | 86 |
PH100 | PLA Polylactic acid | Horizontal 0° | 100 | 81 min | 0.038 | 2604 | 107 |
PHC10 | PLA Polylactic acid | Horizontal 90° | 10 | 60 min | 0.032 | 2390 | 88 |
PHC50 | PLA Polylactic acid | Horizontal 90° | 50 | 62 min | 0.030 | 2664 | 94 |
PHC100 | PLA Polylactic acid | Horizontal 90° | 100 | 94 min | 0.035 | 2851 | 117 |
PV10 | PLA Polylactic acid | Vertical 0° | 10 | 71 min | 0.024 | 2347 | 67 |
PV50 | PLA Polylactic acid | Vertical 0° | 50 | 72 min | 0.024 | 2651 | 74 |
PV100 | PLA Polylactic acid | Vertical 0° | 100 | 97 min | 0.026 | 2691 | 81 |