From: Corrosion mechanisms for lead-barium glass from the Warring States period
Elements
Na2O
MgO
Al2O3
SiO2
K2O
CaO
TiO2
Fe2O3
CuO
PbO
SO3
BaO
ZnO
SrO
0.13
0.43
8.01
63.8
0.37
2.83
0.25
0.87
0.52
20.75
0.29
1.51
0.05
0.12