From: Corrosion mechanisms for lead-barium glass from the Warring States period
Position No. | C | O | Na | Mg | Al | Si | P | S | Cl | Ca | Ti | Fe | Cu | Ba | Pb |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
P1 | 3.02 | 34.42 | Â | Â | 2.39 | 14.61 | 1.94 | 0.73 | Â | 0.94 | 1.96 | 1.51 | Â | Â | 38.47 |
P2 | Â | 27.81 | 1.25 | Â | 1.11 | 19.05 | Â | Â | 1.81 | 0.7 | Â | Â | 1.64 | 10 | 36.63 |
P3 | Â | 48.25 | 0.15 | 0.34 | 3.13 | 37.52 | 0.28 | 0.45 | Â | 1.64 | Â | Â | 0.46 | 0.51 | 7.26 |
P4 | Â | 16.31 | Â | Â | 0.67 | 3.69 | 4.16 | Â | 2.04 | 0.54 | 0.28 | 0.7 | Â | Â | 71.6 |