From: Corrosion mechanisms for lead-barium glass from the Warring States period
Position No. | C | O | Na | Mg | Al | Si | P | S | Cl | K | Ca | Ti | Fe | Cu | Ba | Pb |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
P5 | Â | 27.24 | 1.59 | 0.24 | 0.97 | 18.37 | Â | Â | 1.86 | 0.17 | 0.58 | Â | 0.34 | 1.48 | 9.26 | 37.9 |
P6 | Â | 27.8 | 1.29 | Â | 0.98 | 18.55 | Â | 0.63 | 1.73 | Â | 0.58 | Â | Â | Â | 10.7 | 37.74 |
P7 | Â | 28.42 | 0.96 | 0.23 | 1.32 | 16.95 | Â | 1.76 | 1.15 | Â | 0.68 | Â | Â | 1.46 | 13.82 | 33.25 |
P8 | Â | 29.56 | 0.89 | Â | 1.62 | 17.68 | Â | 2.14 | 1.16 | Â | 0.72 | Â | Â | Â | 15.51 | 30.72 |
P9 | Â | 23.16 | Â | Â | 0.51 | 10 | Â | 3.37 | 0.77 | Â | Â | Â | Â | Â | 37.45 | 24.74 |
P10 | Â | 23.78 | 0.39 | Â | 0.55 | 9.66 | Â | 3.75 | 0.74 | 0.16 | 0.47 | Â | Â | 1.15 | 37.13 | 22.24 |
P11 | Â | 29.6 | Â | Â | 2.68 | 16.38 | 2.19 | Â | 0.84 | Â | 1.06 | 2.2 | 1.67 | Â | Â | 43.36 |
P12 | 7.87 | 53.82 | Â | Â | 3.24 | 25.09 | Â | Â | Â | Â | 1.48 | Â | 0.59 | Â | 0.66 | 7.25 |