Table 1 Characterisation of treatment with E5 and E25 for different samples C1–C8
From: Investigating the effect of nanolime treatment on the drying kinetics of Clipsham limestone
| Â | Sample | \(\Delta m_{d}\) / g | \(\frac{\Delta m_{d}}{V}\) / kg m\(^{-3}\) | \(\Delta L^{*}\) | \(\Delta a^{*}\) | \(\Delta b^{*}\) | \(\Delta E^{*}_{ab}\) | \(R_{a}\) / \(\mu\)m |
|---|---|---|---|---|---|---|---|---|
E5 | C1 | \(-0.001\) \(\pm 0.001\) | \(-0.45\) \(\pm 0.45\) | \(1.71 \pm 2.33\) \(0.52 \pm 2.24\) | \(-0.62 \pm 0.82\) \(-0.43 \pm 0.83\) | \(1.25 \pm 2.69\) \(1.70 \pm 2.60\) | \(2.21 \pm 2.37\) \(1.81 \pm 2.54\) | \(2.63 \pm 0.29\) \(2.30 \pm 0.17\) |
| Â | C2 | \(0.008\) \(\pm 0.001\) | \(2.39\) \(\pm 0.30\) | \(2.40 \pm 2.35\) \(2.61 \pm 2.41\) | \(-0.48 \pm 0.78\) \(-0.43 \pm 0.84\) | \(-2.06 \pm 2.27\) \(-1.90 \pm 2.65\) | \(3.20 \pm 2.29\) \(3.25 \pm 2.48\) | \(2.78 \pm 0.14\) \(2.61 \pm 0.06\) |
| Â | C3 | \(0.002\) \(\pm 0.001\) | \(0.62\) \(\pm 0.31\) | \(5.07 \pm 2.28\) \(4.93 \pm 2.43\) | \(-1.25 \pm 0.77\) \(-1.20 \pm 0.73\) | \(-4.40 \pm 2.34\) \(-4.09 \pm 2.35\) | \(6.83 \pm 2.27\) \(6.52 \pm 2.36\) | \(2.28 \pm 0.05\) \(1.83 \pm 0.11\) |
| Â | C4 | \(-0.001\) \(\pm 0.001\) | \(-0.28\) \(\pm 0.28\) | \(0.18 \pm 2.48\) \(1.47 \pm 2.28\) | \(-0.49 \pm 0.88\) \(-0.72 \pm 0.91\) | \(-4.25 \pm 2.71\) \(-4.26 \pm 2.66\) | \(4.28 \pm 2.70\) \(4.56 \pm 2.59\) | \(2.21 \pm 0.06\) \(1.88 \pm 0.08\) |
E25 | C5 | \(0.006\) \(\pm 0.001\) | \(2.56\) \(\pm 0.43\) | \(2.75 \pm 2.19\) \(1.51 \pm 2.42\) | \(-0.99 \pm 0.79\) \(-0.77 \pm 0.83\) | \(-1.27 \pm 2.55\) \(-0.95 \pm 2.47\) | \(3.19 \pm 2.16\) \(1.94 \pm 2.26\) | \(2.64 \pm 0.16\) \(3.25 \pm 0.29\) |
| Â | C6 | \(0.010\) \(\pm 0.001\) | \(2.92\) \(\pm 0.29\) | \(4.87 \pm 3.96\) \(5.35 \pm 2.42\) | \(-1.21 \pm 1.09\) \(-1.11 \pm 0.83\) | \(-4.89 \pm 2.55\) \(-4.90 \pm 2.47\) | \(7.00 \pm 3.45\) \(7.34 \pm 2.26\) | \(1.97 \pm 0.09\) \(2.41 \pm 0.08\) |
| Â | C7 | \(0.017\) \(\pm 0.001\) | \(4.88\) \(\pm 0.29\) | \(7.38 \pm 3.11\) \(6.23 \pm 3.07\) | \(-1.76 \pm 0.82\) \(-1.60 \pm 0.86\) | \(-5.95 \pm 2.44\) \(-5.41 \pm 2.48\) | \(9.64 \pm 2.82\) \(8.40 \pm 2.78\) | \(2.60 \pm 0.14\) \(1.86 \pm 0.01\) |
| Â | C8 | \(0.032\) \(\pm 0.001\) | \(8.27\) \(\pm 0.26\) | \(11.70 \pm 2.28\) \(11.67 \pm 2.34\) | \(-2.87 \pm 0.76\) \(-2.85 \pm 0.81\) | \(-12.93 \pm 2.21\) \(-12.87 \pm 2.29\) | \(17.67 \pm 2.21\) \(17.60 \pm 2.29\) | \(1.67 \pm 0.03\) \(1.26 \pm 0.21\) |