From: Identification of ancient glass categories based on distance discriminant analysis
 | \({\mathrm{SiO}}_{2}\) | \({\mathrm{Na}}_{2}\mathrm{O}\) | \({\mathrm{K}}_{2}\mathrm{O}\) | \(\mathrm{CaO}\) | \(\mathrm{MgO}\) | \({\mathrm{Al}}_{2}{\mathrm{O}}_{3}\) | \({\mathrm{Fe}}_{2}{\mathrm{O}}_{3}\) |
---|---|---|---|---|---|---|---|
Coefficient | − 0.6703 | 0.1173 | − 0.5832 | − 0.1933 | − 0.0948 | − 0.2411 | − 0.2888 |
\(\mathrm{P value}\) | 5.47e−10 | 0.3445 | 2.23e−10 | 0.1170 | 0.4455 | 0.0493 | 0.0177 |
 | \(\mathrm{CuO}\) | \(\mathrm{PaO}\) | \(\mathrm{BaO}\) | \({\mathrm{P}}_{2}{\mathrm{O}}_{5}\) | \(\mathrm{SrO}\) | \({\mathrm{SnO}}_{2}\) | \({\mathrm{SO}}_{2}\) |
---|---|---|---|---|---|---|---|
Coefficient | − 0.2273 | 0.7695 | 0.7145 | 0.1570 | 0.5881 | 0.0633 | − 0.0649 |
\(\mathrm{P value}\) | 0.0644 | 2.78e−14 | 1.13e−11 | 0.2046 | 1.67e−7 | 0.6110 | 0.6017 |