Steel | Rs (Ω cm2) | CPEcoat-Y1 (S sα1 cm−2) | α1 | Rcoat (Ω cm2) | CPEdl-Y2 (S sα2 cm−2) | α2 | Rct (Ω cm2) |
---|---|---|---|---|---|---|---|
B72 (t = 0) | 3.79E + 03 | 5.70E-10 | 0.96 | 1.08E + 08 | 1.29E-09 | 0.84 | 1.14E + 08 |
B72 (t = 1) | 2.92E + 03 | 4.85E-10 | 0.97 | 3.49E + 06 | 4.89E-09 | 0.59 | 1.39E + 07 |
B72-TiO2 (t = 0) | 2.37E + 03 | 5.21E-10 | 0.96 | 1.04E + 07 | 7.48E-09 | 0.39 | 1.22E + 08 |
B72-TiO2 (t = 1) | 2.49E + 03 | 5.14E-10 | 0.96 | 3.21E + 03 | 2.34E-05 | 0.58 | 1.29E + 04 |
Brass | Rs (Ω cm2) | CPEcoat-Y1 (S sα1 cm−2) | α1 | Rcoat (Ω cm2) | CPEdl-Y2 (S sα2 cm−2) | α2 | Rct (Ω cm2) |
---|---|---|---|---|---|---|---|
B72 (t = 0) | 3.82E + 03 | 5.08E-10 | 0.96 | 6.12E + 07 | 2.76E-09 | 0.42 | 9.29E + 08 |
B72 (t = 1) | 2.68E + 03 | 6.41E-10 | 0.96 | 6.99E + 06 | 1.16E-08 | 0.50 | 8.32E + 07 |
B72-TiO2 (t = 0) | 3.42E + 03 | 6.78E-10 | 0.96 | 6.32E + 06 | 6.44E-09 | 0.53 | 2.55E + 08 |
B72-TiO2 (t = 1) | 2.71E + 03 | 7.28E-06 | 0.54 | 2.68E + 04 | 2.50E-05 | 0.96 | 1.36E + 04 |