From: Archaeometric characterization and restoration proposal for filling mortars of Oshki (Öşvank) church
Basic oxide compounds (%) | H1 | H2 | H3 | H4 | H5 |
---|---|---|---|---|---|
Na2O | 0.600 | 0.800 | 0.083 | 0.270 | 0.650 |
MgO | 1.166 | 1.456 | 1.077 | 1.274 | 1.431 |
Al2O3 | 5.343 | 6.362 | 4.942 | 5.587 | 5.691 |
SiO2 | 37.440 | 43.780 | 35.920 | 40.210 | 40.690 |
P2O5 | 0.0573 | 0.0622 | 0.0508 | 0.057 | 0.079 |
SO3 | 0.085 | 0.114 | 0.056 | 0.084 | 0.066 |
Cl | 0.531 | 0.208 | 0.022 | 0.152 | 0.355 |
K2O | 0.679 | 0.817 | 0.675 | 0.795 | 1.084 |
CaO | 23.230 | 21.770 | 27.560 | 24.030 | 20.600 |
TiO2 | 0.363 | 0.396 | 0.301 | 0.345 | 0.380 |
V2O5 | 0.014 | 0.014 | 0.009 | 0.016 | 0.015 |
Cr2O3 | 0.003 | 0.002 | 0.022 | 0.003 | 0.002 |
MnO | 0.079 | 0.083 | 0.101 | 0.092 | 0.096 |
Fe2O3 | 4.188 | 4.050 | 3.886 | 4.201 | 4.390 |
Loss of ignition | 26.49 | 20.85 | 25.74 | 22.56 | 24.76 |
Total | 100.27 | 100.77 | 100.42 | 99.68 | 100.29 |