From: Corrosion of aircraft heritage: a comparison between modern and historic Duralumin alloys
Sample | Alclad layer thickness, µm | |
---|---|---|
Outer | Inner | |
P-1(p) | 64 ± 3 | 49 ± 2 |
P-2(p) | 30 ± 5 | 35 ± 5 |
P-3(p1) | 82 ± 2a or 40 ± 3b | 48 ± 2 |
P-3(p2) | 109 ± 2 | 146 ± 5a or 70 ± 10b |